|Applications||Recommended for use in 650C-815C Excellent in hot rodding operations. For application where a dry |
Volatile flux is required. Easy clean up.
|Remarks||Equivalent to Handy Dry Flux 6040|
|Applications||It is an all Purpose, low temperature flux for use in brazing both ferrous and non-ferrous metals and alloys |
Using silver brazing filler metals. It begins to melt and dissolve oxides at 340C becomes fully molten
at about 600C and provides adequate protection upto 750C. Excellent in hot rodding operation used
To braze weld where the hot brazing rod is plunged into the dry powder. Easy clean up in hot water.
|Remarks||Equivalent to Esab Rupatam A Flux|
|Applications||The temperature range of thus flux is 600C-925C. It is recommended for brazing tungsten |
Chromium carbides, molybdenum alloys high chromium stainless steels. It is useful where local
Overheating may occur, as in fast induction heating. available in powder paste form.
|Remarks||Equivalent Handy Flux Type B-1|
|Applications||It is general purpose, low temperature flux in paste form which provides creamy smooth consistency and excellent adhesion. |
It begins to melt dissolve oxides at 320C, is fully molten at
600C it provides full protection upto 870C. It is used for brazing all ferrous non-ferrous alloys. Easy clean up with hot water.
|Remarks||Equivalent to Handy Paste Flux.|
|Applications||It is used for brazing or fusion welding of various ferrous non-ferrous metals and alloys ( like cast iron, steel, brass et.) using Cu-Zn (Brass) filler metals.|
|Remarks||Equivalent to Esab Brazotectic Flux.|
|Applications||It is used for brazing various ferrous non-ferrous metals alloys using Cu-Sn (Bronze) based filler metals.|
|Remarks||Equivalent to Esab Bronzotectic Flux.|
|Applications||It is used for brazing aluminium its alloys|
|Remarks||Equivalent to Esab Alotectic Flux.|
|Applications||It is used for welding Cast Iron.|
|Remarks||Equivalent to Esab Castox Flux.|